STYLE NA1001 Compressed Sheet Packing Aramid Fibers

eCatalog Sheet

eCatalog Gaskets

CONSTRUCTION
Style NA1001 is a compressed non-asbestos sheet gasket material produced from a combination of aramid and other synthetic fibers and bonded with nitrile rubber (NBR). It is manufactured through the hot calendar process under rigorous quality control standards that are registered under ISO-9001 certification.

APPLICATION / SERVICE
Style NA1001 is a very good general service gasket material that has numerous applications in the process industries and in the water and wastewater industry. It is also commonly used in equipment such as valves and pumps. Style NA1001 is suitable for service handling the following general media categories:

Mild inorganic acids
Mild organic acids
Concentrated alkalies
Diluted alkalies
Water
Brine

Air
Industrial Gases
Animal oils
Synthetic oils
Vegetable oils
Petroleum and Derivatives

General chemicals
Aliphatic solvents
Aromatic solvents
Oxygenated solvents
Neutral solutions
Refrigerants

PRODUCT DATA

Temperature Limits:

-40°F (-40°C)

720°F (380°C)

Pressure Limits:

Vacuum to 1450 psi (100 bar)

ASTM Line Call Out:

ASTM F104-F713230-M6

Color:

Black

Available Sheet Sizes:

1/32”, 1/16”, 3/32”, 1/8”

59” x 63”

59” x 126”

TYPICAL PHYSICAL PROPERTIES NA1000M

ASTM
TEST METHOD

PHYSICAL PROPERTIES

VALUES

F 36

Compressibility

15%

F 36

Recovery

50%

F 38

Creep Relaxation

37%

F 495

Ignition Loss

32%

F 146

Weight Increase After
Five Hour Immersion

14%

11%

F 146

Thickness Increase After
Five Hour Immersion

9%

9%

F 152

Tensile Strength Across Grain

2900 psi
(20 N/mm²)

Density:

137 lb/ft³
(2.2 gm/cc)

Pressure x Temperature	Sealability Curve

The P x T graph shown above indicates the service limits for this sheet considering pressure and temperature simultaneously...(Tests were performed with nitrogen on 1.6mm thick sheet). The "normal" curve represents the common usage area for this sheet while the "maximum" curve indicates the maximum limits. For applications near or above the "maximum" curve, contact TEADIT.

Properties and application parameters shown are typical and are presented in good faith but no warranty is expressed or implied. This edition supersedes all previous issues and all data is subject to change without notice. 11/96